Chemlok® 487 A/B Adhesive Where to Buy


Product Information

Chemlok® 487 A/B two-component adhesive is used to bond thermoplastic elastomers (TPEs) to metals, glass, plastics (both thermoplastic and thermoset) and other elastomers during injection molding. Chemlok 487 adhesive works well for bonding Santoprene®, Kraton® and Sarlink® thermoplastic elastomers.

When using Chemlok 487 adhesive to mold TPEs to glass, apply Chemlok 144 primer prior to adhesive application.

Shelf Life

Shelf life of each component is one year from date of manufacture when stored by the recipeint at 21-27°C (70-80°F) in original, unopened container.

Chemlok 487 components are moisture sensitive. Minimize exposure to moisture during application and storage.

To help prevent the formation of a gel-like consistency, store Chemlok 487A component above 21°C (70°F). If, however, a gel-like consistency does develop, heat Chemlok 487A component to temperature above 49°C (120°F) and shake material until it returns to a homogeneous liquid.

Features and Benefits

Durable - provides a strong, durable bond that, in many instances, has strength equal to or greater than the elastomer being molded.

Fast Drying - allows for spray application; provides a uniform coating over a large surface area, accelerated solvent evaporation and a shortened drying time.

Versatile - bonds a variety of TPEs to a variety of substrates.

*Data is typical and not to be used for specification purposes.

Auxiliary Products

LORD<sup>®</sup> LokRelease™ 100 Mold Release

fast curing release agent designed for use with molded elastomers

Features and Benefits

Process Enhancer – provides quick, easy part release from molds; single application allows multiple molding cycles; improves molding efficiency in many processes including injection, compression and transfer molding.

Improved Appearance – reduces defects caused by sticking; nontransferable to elastomer compound; does not interfere with compound chemistry.

Environmentally Recommended – contains no Class I or Class II ozone depleting substances; contains no 1,1,1 trichloroethane or methylene chloride.

LORD<sup>®</sup> LokRelease™ 100EZ Mold Release

fast curing, nontransferable release agent

Features and Benefits

Process Enhancer – provides quick, easy part release from molds; single application allows multiple molding cycles; improves molding efficiency in many processes including injection, compression and transfer molding.

Improved Appearance – reduces defects caused by sticking; nontransferable to elastomer compound; does not interfere with compound chemistry.

Environmentally Recommended – contains no Class I or Class II ozone depleting substances; contains no chlorofluorocarbon (CFC) or hydrochlorofluorocarbon (HCFC) propellants; contains no 1,1,1 trichloroethane or methylene chloride.

LORD<sup>®</sup> LokRelease™ 200 Aqueous Mold Release

aqueous mold release is designed for use with molded elastomers

Features and Benefits

Process Enhancer – provides quick, easy part release; produces low build-up, allowing more production time between mold cleanings; improves molding efficiency in many processes including injection, compression and transfer molding.

Improved Appearance – reduces defects caused by sticking; nontransferable, eliminating post-finishing problems.

Environmentally Recommended – water-based coating is engineered to prevent rust and corrosion in steel molds.

LORD<sup>®</sup> LokRelease™ 300 Silicone-Free Mold Release

silicone-free, nontransferable release agent

Features and Benefits

Process Enhancer – provides quick, easy part release; produces low build-up, allowing more production time between mold cleanings; improves mold efficiency in many processes including injection, compression and transfer molding of most rubber compounds including silicone.

Improved Appearance – reduces defects caused by sticking; nontransferable, eliminating post-finishing problems.

Environmentally Recommended – water-based coating is engineered to prevent rust and corrosion in steel molds.

Literature

Download Type Name
Download Safety Data Sheet CHEMLOK 487A
Download Safety Data Sheet CHEMLOK 487B
Download Technical Data Sheet Chemlok 487 A/B Adhesive
Download Selector Guide Chemlok Adhesives Selector Guide

NPS Survey

Product Way-Finding webform
Product Way-Finding webform
Feedback Button
Feedback Button